DIAMETER: 15.5 mm.
COMPOSITION: Stainless steel alloy.
This alloy is composed as follows:
between
16% and 18%, of chromium;
0.75%
of nickel, maximum;
0.12%
of carbon, maximum;
1% of
silicon, maximum;
1% of
manganese, maximum;
0.03%
of sulfur, maximum;
0.04%
of phosphorus, maximum;
and the
remaining of iron.
WEIGHT: 1.58 g
DIAMETER: 17.0 mm
COMPOSITION: Stainless steel alloy.
This alloy is composed as follows:
between
16% and 18% , of chromium;
0.75%
of nickel, maximum;
0.12%
of carbon, maximum;
1% of
silicon, maximum;
1% of
manganese, maximum;
0.03%
of sulfur, maximum;
0.04%
of phosphorus, maximum;
and the
remaining of iron.
WEIGHT: 2.08 g
DIAMETER: 19.5 mm
COMPOSITION: Bronze-aluminum alloy.
This alloy is composed as follows:
92% of
copper;
6% of
aluminum; and
2% of
nickel.
WEIGHT: 3.04 g
DIAMETER: 22.0 mm
COMPOSITION: Bronze-aluminum alloy.
This alloy is composed as follows:
92% of
copper;
6% of
aluminum; and
2% of
nickel;
WEIGHT: 4.39 g
DIAMETER: 21.0 mm
COMPOSITION: This coin will be bimetallic and composed by two
alloys; one for its
central part and other its perimetrical ring as described below:
1. Central part of the coin.
This alloy is composed as follows:
92% of
copper;
6% of
aluminum; and
2% of
nickel;
2. Perimetrical ring of the coin.
This alloy is composed as follows:
between
16% and 18% , of chromium;
0.75%
of nickel, maximum;
0.12%
of carbon, maximum;
1% of
silicon, maximum;
1% of
manganese, maximum;
0.03%
of sulfur, maximum;
0.04%
of phosphorus, maximum;
and the
remaining of iron.
TOTAL WEIGHT: 3.95 g
DIAMETER: 23.0 mm
COMPOSITION: This coin will be bimetallic and composed by two alloys;
one
for its central part and other for its perimetrical ring as described
below:
1. Central part of the coin.
This alloy is composed as follows:
92% of
copper;
6% of
aluminum; and
2% of
nickel;
2. Perimetrical ring of the coin.
This alloy is composed as follows:
between
16% and 18% , of chromium;
0.75%
of nickel, maximum;
0.12%
of carbon, maximum;
1% of
silicon, maximum;
1% of
manganese, maximum;
0.03%
of sulfur, maximum;
0.04%
of phosphorus, maximum;
and the
remaining of iron.
TOTAL WEIGHT: 5.19 g
DIAMETER: 25.5 mm
COMPOSITION: This coin will be bimetallic and composed by two
alloys; one
for its central part and other for its perimetrical ring as described
below:
1. Central part of the coin.
This alloy is composed as follows:
92% of
copper;
6% of
aluminum; and
2% of
nickel;
2. Perimetrical ring of the coin.
This alloy is composed as follows:
between
16% and 18% , of chromium;
0.75%
of nickel, maximum;
0.12%
of carbon, maximum;
1% of
silicon, maximum;
1% of
manganese, maximum;
0.03%
of sulfur, maximum;
0.04%
of phosphorus, maximum;
and the
remaining of iron.
TOTAL WEIGHT: 7.07 g
DIAMETER: 28.0 mm
COMPOSITION: This coin will be bimetallic and composed by two
alloys; one
for its central part and other for its perimetrical ring as described
below:
1. Central part of the coin. It could
be composed by any of the following
alloys:
A) Sterling
silver alloy.
Fineness: 0.925.
Alloyed metal: Copper
Content: 1/6 oz. of pure silver.
B) German
silver alloy.
Content: 65% of copper, 10% of nickel and 25% of zinc.
2. Perimetrical ring of the coin.
This alloy is composed as follows:
between
16% and 18% , of chromium;
0.75%
of nickel, maximum;
0.12%
of carbon, maximum;
1% of
silicon, maximum;
1% of
manganese, maximum;
0.03%
of sulfur, maximum;
0.04%
of phosphorus, maximum;
and the
remaining of iron.
TOTAL WEIGHT: The total weight will be the sum of central and
perimetrical
weights which will correspond:
Type A) 11.183 g
Type B) 10.329 g
DIAMETER: 32.0 mm
COMPOSITION: This coin will be bimetallic and composed by two
alloys; one
for its central part and other for its perimetrical ring as described
below:
1. Central part of the coin.
Silver: Sterling, 0.925
Alloyed metal: Copper
Weight: 8.406 g
Content: 1/4 oz. of pure silver.
2. Perimetrical ring of the coin.
between
16% and 18% , of chromium;
0.75%
of nickel, maximum;
0.12%
of carbon, maximum;
1% of
silicon, maximum;
1% of
manganese, maximum;
0.03%
of sulfur, maximum;
0.04%
of phosphorus, maximum;
and the
remaining of iron.
TOTAL WEIGHT: 16.996 g
DIAMETER: 39.0 mm
COMPOSITION: This coin will be bimetallic and composed by two
alloys; one
for its central part and other for its perimetrical ring as described
below:
1. Central part of the coin.
Silver: Sterling, 0.925
Alloyed metal: Copper
Weight: 16.812 g
Content: 1/2 oz. of pure silver.
2. Perimetrical ring of the coin.
between
16% and 18% , of chromium;
0.75%
of nickel, maximum;
0.12%
of carbon, maximum;
1% of
silicon, maximum;
1% of
manganese, maximum;
0.03%
of sulfur, maximum;
0.04%
of phosphorus, maximum;
and the
remaining of iron.
TOTAL WEIGHT: 33.967 g